High Purity Alumina
Product Name
High Purity Alumina
Image
Gibbsite/Boehmite
Super Fine Powder | Unit | Gibbsite | Boehmite | ||
---|---|---|---|---|---|
SAFH-05 | SAFL-05 | SAFB-05 | |||
Al(OH)3 | Al(OH)3 | AlOOH | |||
Purity | % | 99.5 | 99.7 | 99.5 | |
Impurity | Na2O | % | 0.4 | 0.25 | 0.4 |
SiO2 | % | 0.03 | 0.03 | 0.03 | |
Fe2O3 | % | 0.01 | 0.01 | 0.01 | |
W-Na2O | % | 0.13 | 0.06 | 0.13 | |
Loss on Drying | % | 0.4 | 0.4 | 0.4 | |
Loss on Ignition | % | 34.5 | 34.5 | 17 | |
Density | Loosed | g/cm2 | 0.1-0.2 | 0.1-0.2 | 0.1-0.2 |
Packed | g/cm2 | 0.3-0.4 | 0.3-0.4 | 0.3-0.4 | |
Mean Siza | Dp50 | μm | 0.4-0.6 | 0.4-0.6 | 0.4-0.6 |
+45μm | % | 0.0 | 0.0 | 0.0 | |
Whiteness | % | 98 | 98 | 98 | |
Specific Surface Area |
m2/g | 8 | 8 | 7 | |
DOP Oil Absorption | ml/100g | 55 | 55 | 55 | |
Electric Conductivity | ms/cm | 800 | 200 | 800 | |
True Density | 2.42 | ||||
Refractive Index | 1.57 | ||||
Mohs Hardness | 3 | ||||
Application | Separator coating, Flame Retardant, Paper Surface |
Alumina
Super Fine Powder | Unit | Alumina | |||
---|---|---|---|---|---|
SAFG-03 | SAFA-05 | ||||
γ-Al2O3 | α-Al2O3 | ||||
Purity | % | 99.6 | 99.6 | ||
Impurity | Na2O | % | 99.6 | 99.6 | |
SiO2 | % | 0.3 | 0.3 | ||
Fe2O3 | % | 0.01 | 0.01 | ||
MgO | % | 0.05 | 0.05 | ||
Loss on Drying | % | 0.4 | 0.4 | ||
Loss on Ignition | % | 0.1 | 0.1 | ||
Bulk Density | g/cm2 | 0.1-0.2 | 0.1-0.2 | ||
Mean Size | Dp50 | μm | 0.2-0.4 | 0.4-0.6 | |
+45μm | % | 0.0 | 0.0 | ||
Whiteness | % | 99 | 99 | ||
Specific Surface Area |
m2/g | 12 | 8 | ||
Application | Separator coating |
Plate-shape Power | Alumina | |||
Unit | SAPS-20 | SAPS-20 | ||
---|---|---|---|---|
α-Al2O3 | α-Al2O3 | |||
Heavy metal (ICP) |
Pb | mg/kg | 20 | 20 |
Sb | mg/kg | 10 | 10 | |
Cd | mg/kg | 5 | 5 | |
As | mg/kg | 5 | 5 | |
Hg | mg/kg | 1 | 1 | |
Loss on Drying | % | 1 | 1 | |
Mean Size(Dp50) | μm | 5-10 | 10-20 | |
Application | Cosmetic, Paint pearl |
High Purity Alumina
High Purity Alumina Powder |
Unit | High Putiry Alumina | |
---|---|---|---|
SAHD-10 | |||
α-Al2O3 | |||
Purity | % | 99.998 | |
Impurity | Na | mg/kg | 7 |
Si | mg/kg | 7 | |
Fe | mg/kg | 3 | |
Ca | mg/kg | 1 | |
Mg | mg/kg | 1 | |
Cu | mg/kg | 1 | |
Bulk Density | Loosed | g/cm2 | 0.4 |
Packed | g/cm2 | 0.8 | |
Mean Size (Dp50) | μm | 0.7-0.9 |